| Item | Best price and quality liquid Fiberglass unsaturated polyester resin for FRP pipes and tank |
| Appearance | Light green liquid |
| Usage | pipes and tank and other FRP products |
| Technilogy | Hand paste/winding/ spray |
| Proportion of hardener | 1.5% ~2.0% adjustable according to the temperature |
| Proportion of accelerator | 0.8-1.5% of resin |
| Feature 1 | Moderate viscosity and reactivity |
| Feature 2 | Curing good rigidity, high mechanical properties |
Performance index of liquid unsaturated polyester resin 181 frp resin used for pipeline and septic tank
| performance |
parameter |
unit |
standard test |
| Appearance |
Light green liquid |
- |
|
| Acid value |
17-25 |
mgKOH/g |
GB/T 2895-2008
|
| Solid content |
61-67 |
% |
GB/T 7193-2008 |
| Viscosity25℃ |
0.3-0.6 |
pa.s |
GB/T 7193-2008 |
| stability80℃
|
≥24 |
h |
GB/T 7193-2008 |
| Typical curing properties |
25 ° C water bath, 100g resin plus 2ml methyl ethyl ketone peroxide solution and 4ml cobalt isooctanoate solution |
- |
- |
| Gel time |
8-18 |
min |
GB/T 7193-2008 |
Resin Casting Properties of Fiberglass unsaturated polyester resin for FRP pipes and tank
| performance |
parameter |
unit |
standard test |
| Appearance |
Casting with no blemish |
- |
|
| Barcol hardness |
42 |
Hba |
GB/T 3854 |
| Tensile Strength |
60 |
Mpa |
GB/T 2567-2008 |
| Tensile modulus of elasticity |
3800 |
Mpa |
GB/T 2567-2008 |
| Elongation at break |
2 |
% |
GB/T 2567-2008 |
| Bending strength |
110 |
MPa |
GB/T 2567-2008 |
| Bending elastic modulus |
3900 |
MPa |
GB/T 2567-2008 |
| Impact strength |
12 |
KJ/m2 |
GB/T 2567-2008 |
| Heat distortion temperature |
70 |
℃ |
GB/T 1634-2004 |
| Pasteurian hardness |
68 |
- |
GB/T 3854-2005 |
| Absorbability |
0.15 |
% |
GB/T 1034-2008 |
Selling Units:Single item
Single package size: 43X38X30 cm
Single gross weight:22.000 kg
Package Type:1kg ,5kg,20kg 25kg per bottle/20kg per set/200kg per bucket
Unless otherwise specified, the Unsaturated Polyester resin products should be stored in a dry, cool and moisture proof area. Best used within 12 months after production date. The Unsaturated Polyester resin should remain in their original packaging until just prior to use. The Unsaturated Polyester resin products are suitable for delivery by the way of ship, train, or truck.